China quality refractory Cordierite kiln shelf 500*450*15mm for fire ceramics
1. Introduction
Cordierite ceramics are well known for their low thermal expansion and refractory character. Although cordierite is available as a powder, when we use the term we are generally talking about ceramic that went into the kiln as ordinary composite of ceramic powders but emerges as a cordierite crystalline matrix (grown by the firing process tuned to its needs).
Cordierite makes the ceramic manufacture of products like catalytic converters possible. They constantly heat up and cool down quickly and must not crack because of the shock. These converters get their thermal shock resistance properties from a bonded matrix of low-expansion cordierite crystals. These crystals form during firing between 1300 to 1400C (interestingly, cordierite crystals have a lesser thermal expansion along one axis than another). Thus, the better the density of the precursor mix and controlled the firing the better the properties of the cordierite material are.
Extruded kiln shelf
Extruded kiln shelf have holes running the length of the cross section and are manufactured using high pressure vacuum extrusion. They are used mainly in the sanitary ware and glass panel industries.
2. Characteristics:
Excellent energy savings
Lighter weight and higher load capacity
Excellent distortion resistance at high temperature
Suitable for faster firings with better bearing capacity for hot and cold extremes
Plain kiln shelf
Plain kiln shelf are the most common type of primary kiln furniture, usually produced by semi-dry pressing, but can also be made by pressure-casting. There are extra large kiln shelf , extra kiln shelf, plain kiln shelf, perforated kiln shelf, grooved kiln shelf,trapezoid kiln shelf, round kiln shelf and special kiln shelf.
Plain Supports
Extruded Tubes
Fittings
Secondary Kiln Furniture
Sagger and Crucibles
Kiln Accessories
3. Product specification
|
Item and Descriptions
|
Specifications Offered
|
|
Al2O3 (%)
|
40~48
|
|
SiO2 (%)
|
45~48
|
|
MgO (%)
|
5~8
|
|
MOR(MPa)
|
20℃
|
14
|
|
1250℃
|
12
|
|
Bulk Density(g/cm3)
|
2.0
|
|
Open Porosity(%)
|
28
|
|
Phase composition(%)
|
Mullite
|
55
|
|
Cordierite
|
30
|
|
Max. Service temperature ℃
|
1280
|
WE HAVE PROFESSIONAL DETECTING EQUIPMENT
We are aimed to improve R&D and production process and equipment. Moreover, we cooperate with famous university such like Liaoning University of Science and Technology, Beijing University of Science and Technology.
We promise:
- We will offer our best price.
- Your inquiry will be replied within 24 hours.
- Experienced staff can give you professional suggestions.
- We ensure you high quality products and timely delivery.
- We offer complete and good after-sale service.